F904L UNS N08904 Studs Bolts W.Nr.1.4539 for Sale

F904L UNS N08904 Studs Bolts W.Nr.1.4539 for Sale

904L (NO8904) Studs 904L studs is a metal rod or bar with threads on both sides. It also known as double-headed screws or studs, used to connect two parts together. General for mining machinery, bridges, cars, motorcycles, boiler steel structure, hanging tower, large span steel structure and...

    904L (NO8904) Studs
    904L studs is a metal rod or bar with threads on both sides. It also known as double-headed screws or studs, used to connect two parts together. General for mining machinery, bridges, cars, motorcycles, boiler steel structure, hanging tower, large span steel structure and large buildings. 

    We tend to use studs when the parts need to remove frequently, because the thread will be worn if install and remove often, then we need to change the studs.

    904L is a very low carbon containing high alloy austenitic stainless steel. The steel designed for the harsh corrosion conditions. 904L has been standardized in many countries now, and have already been approved in the manufacture of pressure vessels.
    904L Corrosion resistance
    Since the 904L carbon content is very low (up to 0.020%), there is no carbide precipitation in the case of general heat treatment and welding. This eliminates the risk of intergranular corrosion that occurs after general heat treatment and welding. Due to the high chromium nickel molybdenum content and the addition of copper, 904L can be passivated even in a reducing environment such as sulfuric acid and formic acid. High nickel content in the active state also has a lower corrosion rate. In the range of 0 to 98% pure sulfuric acid, 904L of the use of the temperature can be as high as 40 degrees Celsius. In the range of 0 ~ 85% concentration of pure phosphoric acid, its corrosion resistance is very good. In the industrial process of phosphoric acid produced by the wet process, the impurities have a strong influence on the corrosion resistance. In all the phosphoric acid, 904L corrosion resistance is better than ordinary stainless steel. In strong oxidizing nitric acid, 904L has a lower corrosion resistance than a highly alloyed steel free of molybdenum. In hydrochloric acid, the use of 904L is limited to a lower concentration of 1-2%. In this concentration range. 904L corrosion resistance is better than conventional stainless steel. 904L steel has a high resistance to corrosion resistance. In the chloride solution, its resistance to crevice corrosion is also very good. 904L high nickel content, reducing the corrosion rate in the pit and the gap. Ordinary austenitic stainless steels may be sensitive to stress corrosion in a chloride-rich environment at temperatures above 60 ° C, which can be reduced by increasing the nickel content of stainless steel. Due to the high nickel content, 904L has a high resistance to stress corrosion cracking in chloride solutions, concentrated hydroxide solutions and hydrogen sulfide-rich environments.
    904L Chemical compositon:

    Alloy

    %

    Ni

    Cr

    Mo

    Cu

    Fe

    C

    Mn

    Si

    P

    S

    904L

    Min.

    23

    19

    4

    1

    Balance






    Max.

    28

    23

    5

    2

    0.02

    2

    1

    0.045

    0.035

    904L Physical properties:

    Density

    8.0 g/cm3

    Melting point

    1300-1390 ℃

    904L Alloy minimum mechanical properties in the room temperature:

    Alloy

    Tensile strength
    Rm N/mm2

    Yield strength
    RP0.2N/mm2

    Elongation
     A5 %

    904L

    490

    216

    35

    If our f904l uns n08904 studs bolts w.nr.1.4539 for sale caters to your requirement, welcome to contact our professional manufacturers and suppliers. Highly qualified products, competitive price and good after-sale service can be assured.