SUS316L SS316L 1.4404 Heavy Hex Nut

SUS316L SS316L 1.4404 Heavy Hex Nut

SS316L Nut The nut is a fastener with internal threads and used in conjunction with a screw for mechanical parts for movement or power. BDF can offer all kinds of hot forged and cold formed nuts such as hexagon nuts, heavy hex nuts, hexagon coupling nuts, hexagon thin nuts, hexagon castle nuts,...

    SS316L Nut
    The nut is a fastener with internal threads and used in conjunction with a screw for mechanical parts for movement or power.

    BDF can offer all kinds of hot forged and cold formed nuts such as hexagon nuts, heavy hex nuts, hexagon coupling nuts, hexagon thin nuts, hexagon castle nuts, self locking nuts, hexagon domed cap nuts and other non-standard nuts according to customer drawings. The size ranges from M6-M100 in METRIC and 3/8” to 3-1/2” in INCH.
    316L alloy has the following characteristics: 1) cold rolled product appearance of good gloss, beautiful; 2) due to the addition of Mo, corrosion resistance, especially pitting corrosion resistance is excellent; 3) excellent high temperature strength 4) Excellent work hardening (Weak magnetic after processing) 5) solid solution state without magnetic;
    Compared to chromium-nickel austenitic stainless steels, 316L stainless steel offers higher creep, stress to rupture and tensile strength at elevated temperatures.These alloys may be considered for a wide variety of applications where one or more properties are important.
    SS316L Chemical Composition:

    %

    Ni

    Cr

    C

    Mn

    Si

    P

    S

    Mo

    Min

    10.0

    16.0






    2.0

    Max

    14.0

    18.0

    0.03

    2.0

    1.0

    0.045

    0.03

    3.0

    Physical properties:

    Density

    7.98 g/cm3

    Melting range

    1375~1450℃

    316L Mechanical Properties:

    Temper

    Annealed

    Cold worked (approx. 20%)

    Material

    316

    316L


    316

    316L


    Tensile Rm

    75

    70

    ksi (min)

    102-131

    ksi (min)

    Tensile Rm

    515

    485

    MPa (min)

    700-900

    MPa (min)

    R.p. 0.2% Yield

    30

    27

    ksi (min)

    73-102

    ksi (min)

    R.p. 0.2% Yield

    205

    182

    MPa (min)

    500-700

    MPa (min)

    Elongation (2” or 4D gl)

    35

    % (min)

    40

    % (min)

    SS316L minimum mechanical properties in the room temperature:

    Alloy state

    Tensile strength Rm N/mm²

    Yield strength RP 0. 2N/mm²

    Elongation A 5 %

    HRC(HBS)

    solution

    485

    170

    30

    ≤187